&control
    calculation  = 'nscf',
    restart_mode = 'from_scratch',
    prefix       = 'MoS2-2H',
    pseudo_dir   = '/home/rehnd/.local/espresso-5.2.0/pseudo',
    outdir       = '../out',

    wf_collect    = .true.
    verbosity     = 'high'
    forc_conv_thr = 0.01D-3
    etot_conv_thr = 1D-6
/
&system
    ibrav       = 4,
    celldm(1)   = 6.02882349219,
    celldm(3)   = 4.66380258256,
    nat         = 6,
    ntyp        = 2,
    ecutwfc     = 37,
    occupations = 'smearing',
    degauss     = 0.005
    ! vdw_corr    = 'dft-d'
    ! tot_charge  = 0.5
/
&electrons
    conv_thr         = 1.0e-10
    electron_maxstep = 100,
    mixing_mode      = 'plain'
    mixing_beta      = 0.1
    !diagonalization  ='cg'
/

ATOMIC_SPECIES
S  32.065  S.pbe-mt_fhi.UPF
Mo 95.94  Mo.pbe-mt_fhi.UPF

ATOMIC_POSITIONS {crystal}
S     0.333333000   0.666667000   0.144245583
S     0.666667000   0.333333000   0.644245583
S     0.333333000   0.666667000   0.355754417
S     0.666667000   0.333333000   0.855754417
Mo    0.666667000   0.333333000   0.250000000
Mo    0.333333000   0.666667000   0.750000000

K_POINTS {automatic}
12 12 12 0 0 0


! Original ATOMIC_POSTIIONS
! S  0.333333 0.666667 0.144826
! S  0.666667 0.333333 0.644826
! S  0.333333 0.666667 0.355174
! S  0.666667 0.333333 0.855174
! Mo 0.666667 0.333333 0.250000
! Mo 0.333333 0.666667 0.750000